PC(聚碳酸酯)HS3025G10/Samyang(三养)物性表参数-喜好网-记录每日喜好的科技时尚娱乐生活

Samyang(三养)TRIREX PC HS3025G10是一种GF强化,冲击补强聚碳酸酯，比重是1.25g/cm³，熔流率（熔体流动速率）(300°C/1.2 kg)13g/10min，有着优异的机械特性，很好的尺寸稳定性及良好的电气特性，应用于电子电器。

PC HS3025G10

以下是PC(聚碳酸酯)HS3025G10/Samyang(三养)物性表参数

PROPERTY	UNIT	ASTM METHOD	TYPICAL DATA
Physical
Specific Gravity	-	D792	1.25
Water Absorption (24 hours at 23℃)	%	D570	0.12
Melt Flow Rate (300℃, 1.2kg)	g/10min	D1238	13
MECHANICAL
Tensile Strength at yield	kgf/㎠	D638	600
Tensile Elongation at break	%	D638	6
Flexural Strength at yield	kgf/㎠	D790	1,000
Flexural Modulus	kgf/㎠	D790	30,000
Izod Impact Strength, notched, 23℃ (1/8”)	kgf∙㎝/㎝	D256	14
Rockwell Hardness	R scale	D785	121
THERMAL
HDT, 18.6 ㎏f/㎠	℃	D648	124
Coefficient of Linear Thermal Expansion	㎜/㎜/℃	D696	3.2 x 10-5
ELECTRICAL
Volume Resistivity	Ω∙㎝	D257	4E+16
Dielectric Strength	kV/㎜	D149	19
Dielectric Constant	-	D150	3.11
Dissipation Factor	-	D150	0.0097
ARC Resistance	sec	D495	120
OTHERS
UL-94 Flammability (0.75mm thickness)	-	(UL 94)	HB
Mold Shrinkage (3mm thickness)	%	D955	0.2~0.4

※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIREX® HS3025G10 GRADE

General processing conditions for TRIREX® HS3025G10 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION	UNIT	CONDITIONS
Drying Temperature	℃	120
Drying Time	hr	3~4
Moisture Content, Max	%	0.02
Melt Temperature	℃	310~330
Nozzle Temperature	℃	300~320
Front Temperature	℃	300~320
Middle Temperature	℃	290~310
Rear Temperature	℃	280~300
Mold Temperature	℃	80~110