PC(聚碳酸酯)HS3022G30/Samyang(三养)物性表参数-喜好网-记录每日喜好的科技时尚娱乐生活

Samyang(三养)TRIREX PC HS3022G30是一种GF强化,冲击补强聚碳酸酯，比重是1.35g/cm³，熔流率（熔体流动速率）(300°C/1.2 kg)1g/10min，有着优异的机械特性，很好的尺寸稳定性及良好的电气特性，应用于电子电器。

PC HS3022G30

以下是PC(聚碳酸酯)HS3022G30/Samyang(三养)物性表参数

PROPERTY	UNIT	ASTM METHOD	TYPICAL DATA
Physical
Specific Gravity	-	D792	1.35
Water Absorption (24 hours at 23℃)	%	D570	0.12
Melt Flow Rate (300℃, 1.2kg)	g/10min	D1238	1
MECHANICAL
Tensile Strength at yield	kgf/㎠	D638	1,000
Tensile Elongation at break	%	D638	3
Flexural Strength at yield	kgf/㎠	D790	1,500
Flexural Modulus	kgf/㎠	D790	65,000
Izod Impact Strength, notched, 23℃ (1/8”)	kgf∙㎝/㎝	D256	15
Rockwell Hardness	R scale	D785	122
THERMAL
HDT, 18.6 ㎏f/㎠	℃	D648	126
Coefficient of Linear Thermal Expansion	㎜/㎜/℃	D696	2.3 x 10-5
ELECTRICAL
Volume Resistivity	Ω∙㎝	D257	4E+16
Dielectric Strength	kV/㎜	D149	19
Dielectric Constant	-	D150	3.11
Dissipation Factor	-	D150	0.0097
ARC Resistance	sec	D495	120
OTHERS
UL-94 Flammability (0.75mm thickness)	-	(UL 94)	HB
Mold Shrinkage (3mm thickness)	%	D955	0.1~0.3

※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIREX® HS3022G30 GRADE

General processing conditions for TRIREX® HS3022G30 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION	UNIT	CONDITIONS
Drying Temperature	℃	120
Drying Time	hr	3~4
Moisture Content, Max	%	0.02
Melt Temperature	℃	290~310
Nozzle Temperature	℃	290~315
Front Temperature	℃	280~315
Middle Temperature	℃	275~300
Rear Temperature	℃	260~280
Mold Temperature	℃	65~105
Back Pressure	MPa	0.3~0.7
Screw Speed	rpm	40~70
Vent Depth	mm	0.02~0.08